Repetitive ultrafast melting of InSb as an x-ray timing diagnostic

Författare:
Publiceringsår: 2008
Språk: Engelska
Sidor: 103510-6 pp
Publikation/Tidskrift/Serie: Journal of Applied Physics
Volym: 103
Nummer: 10
Dokumenttyp: Artikel
Förlag: American Institute of Physics

Sammanfattning

We have demonstrated the possibility of using repetitive ultrafast melting of InSb as a timing diagnostic in connection with visible-light pump/x-ray probe measurements at high-repetition-rate x-ray facilities. Although the sample was molten and regrown approximately 1x10(6) times, a distinct reduction in time-resolved x-ray reflectivity could be observed using a streak camera with a time resolution of 2.5 ps. The time-resolved x-ray reflectivity displayed this distinct decrease despite the fact that the average reflectivity of the sample had fallen to approximately 50% of its original value due to accumulated damage from the prolonged laser exposure. The topography of the laser-exposed sample was mapped using an optical microscope, a stylus profilometer, photoelectron microscopy, and a scanning tunneling microscope. Although the surface of the sample is not flat following prolonged exposure at laser fluences above 15 mJ/cm(2), the atomic scale structure regrows, and thus, regenerates the sample on a nanosecond timescale. In the fluence range between 15 and 25 mJ/cm(2), the laser power is sufficient to melt the sample, while regrowth occurs with a sufficiently good structure to allow the extraction of timing information via ultrafast time-resolved x-ray measurements. This can be applied for timing purposes at synchrotron radiation and x-ray free-electron laser facilities. It is also noteworthy that we were able to reproduce the fluence dependencies of melting depth and disordering time previously obtained in single-shot, nonthermal melting experiments with higher temporal resolution.

Disputation

Nyckelord

  • Physics and Astronomy

Övriga

Published
Yes
  • ISSN: 0021-8979

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen