GaAs/GaSb nanowire heterostructures grown by MOVPE

Författare:
Publiceringsår: 2008
Språk: Engelska
Sidor: 4115-4121
Publikation/Tidskrift/Serie: JOURNAL OF CRYSTAL GROWTH
Volym: 310
Nummer: 18
Dokumenttyp: Artikel
Förlag: ELSEVIER SCIENCE BV

Sammanfattning

We report Au-assisted growth of GaAs/GaSb nanowire heterostructures on GaAs(1 1 1)B-substrates by metal-organic vapor phase epitaxy. The growth is studied at various precursor molar fractions and temperatures, in order to optimize the growth conditions for the GaSb nanowire segment. In contrast to most other III-V nanowire systems, the GaSb nanowire growth is Group V-limited under most conditions. We found that depending on the TMSb molar fraction, the seed particle is either supersaturated AuGa or AuGa2 during GaSb growth. The high Ga content in the particle gives a characteristic diameter increase between the GaAs and GaSb segment. From TEM and XEDS measurements we conclude that the GaSb nanowire growth occurs along either the AuGa-GaSb or AuGa2-GaSb pseudo-binaries of the Au-Ga-Sb ternary phase diagram. Finally, the GaSb nanowires exhibit untapered radial growth on the {1 (1) over bar 0} side facets. (C) 2008 Elsevier B.V. All rights reserved.

Disputation

Nyckelord

  • Physics and Astronomy
  • gallium antimonide
  • antimonides
  • metal-organic vapor phase epitaxy
  • nanowires
  • heterostructures

Övriga

Published
Yes
  • Nano
  • ISSN: 0022-0248

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen