Enhanced Sb incorporation in InAsSb nanowires grown by metalorganic vapor phase epitaxy

Författare:
Publiceringsår: 2011
Språk: Engelska
Sidor:
Publikation/Tidskrift/Serie: Applied Physics Letters
Volym: 98
Nummer: 11
Dokumenttyp: Artikel
Förlag: Amer Inst Physics

Sammanfattning

We demonstrate metalorganic vapor phase epitaxy of InAs1-xSbx nanowires (x=0.08-0.77) for applications in high-speed electronics and long-wavelength optical devices. The composition of the InAsSb nanowires and InAsSb epilayers on the same sample is independently determined using lab-setup high resolution x-ray diffraction, by making use of the size-dependent in-plane broadening of the nanowire Bragg peak. We find that the incorporation of Sb into the nanowires is significantly higher than for planar epitaxy under the same growth conditions. Thermodynamic calculations indicate that this is due to a dramatically decreased effective V/III ratio at the particle/nanowire interface. (C) 2011 American Institute of Physics. (C) doi: 10.1063/1.3566980

Disputation

Nyckelord

  • Physics and Astronomy

Övrigt

Published
Yes
  • Nano
  • ISSN: 0003-6951

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen

LERU logo U21 logo