Synthesis and decomposition mechanisms of ternary Mg2COH5 studied using in situ synchrotron X-ray diffraction

Författare:
  • M. Norek
  • T. K. Nielsen
  • M. Polanski
  • I. Kunce
  • T. Plocinski
  • L. R. Jaroszewicz
  • Yngve Cerenius
  • T. R. Jensen
  • J. Bystrzycki
Publiceringsår: 2011
Språk: Engelska
Sidor: 10760-10770
Publikation/Tidskrift/Serie: International Journal Of Hydrogen Energy
Volym: 36
Nummer: 17
Dokumenttyp: Artikel
Förlag: Pergamon-Elsevier Science Ltd

Sammanfattning

A ternary Mg2COH5 hydride was synthesized using a novel method that relies on a relatively short mechanical milling time (1 h) of a 2:1 MgH2-Co powder mixture followed by sintering at a sufficiently high hydrogen pressure (>85 bar) and heating from RT to 500 degrees C. The ternary hydride forms in less than 2.5 h (including the milling time) with a yield of similar to 90% at similar to 300 degrees C. The mechanisms of formation and decomposition of ternary Mg2COH5 were studied in detail using an in situ synchrotron radiation powder X-ray diffraction (SR-PXD). The obtained experimental results are supported by morphological and microstructural investigations performed using SEM and high-resolution STEM. Additionally, thermal effects occurring during the desorption reaction were studied using DSC. The morphology of as-prepared ternary Mg2COH5 is characterized by the presence of porous particles with various shapes and sizes, which, in fact, are a type of nanocomposite consisting mainly of nanocrystallites with a size of similar to 5 nm. Mg2COH5 decomposes at approximately 300 degrees C to elemental Mg and Co. Additionally, at approximately 400 degrees C, MgCo is formed as precipitates inserted into the Mg Co matrix. During the rehydrogenation of the decomposed residues, prior to the formation of Mg2COH5, MgH2 appears, which confirms its key role in the synthesis of the ternary Mg2COH5. Copyright (C) 2011, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

Disputation

Nyckelord

  • Physics and Astronomy
  • Magnesium-cobalt hydride
  • Synthesis
  • Mechanical milling
  • In situ
  • SR-PXD
  • Microstructure

Övriga

Published
Yes
  • ISSN: 0360-3199

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen