Electron microscopy study of single crystal BaZr0.9Y0.1O3-x films prepared by chemical solution deposition
Författare
Summary, in English
Single crystal thin films of 10% yttrium doped barium zirconate (BZY10) have been prepared using chemical solution deposition on magnesium oxide substrates and annealed at 800 or 1000 degrees C. A focused ion beam lift out technique was used to prepare thin (< 100 nm) specimens for transmission electron microscopy (TEM) analysis. A variety of TEM based techniques were used for characterization, including high resolution imaging, X-ray energy dispersive spectroscopy and energy filtered TEM. High resolution TEM imaging indicated a high quality single crystal film with an epitaxial cube on cube type interface between BZY10 and MgO. For the sample annealed 1000 degrees C, annular dark field imaging in scanning transmission electron microscopy (STEM) mode showed a layered pattern of lower intensity in the single crystal film. Energy filtered TEM thickness map together with scanning electron microscopy (SEM) indicate the pattern consists of partially repeating voids.
Avdelning/ar
Publiceringsår
2012
Språk
Engelska
Sidor
121-127
Publikation/Tidskrift/Serie
ECS Transactions
Volym
45
Issue
1
Dokumenttyp
Konferensbidrag
Förlag
Electrochemical Society
Ämne
- Chemical Sciences
Conference name
Symposium on Ionic and Mixed Conducting Ceramics 8
Conference date
2012-05-06 - 2012-05-10
Status
Published
ISBN/ISSN/Övrigt
- ISSN: 1938-5862
- ISSN: 1938-6737