On the intumescence of ethylene-acrylate copolymers blended

Författare

Summary, in English

The combustion and melt dripping of poly(ethylene-co-butyl acrylate) (EBA), EBA blended with polypropylene (EBAePP) and poly (ethylene-co-methacrylic acid) (EMAA), each blended with calcium carbonate and polydimethylsiloxane, were studied. In situ measurement of the temperature gradient in the cone calorimeter were combined with infrared spectroscopy measurements on specimens withdrawn and quenched at different times of the experiment. The reactions that govern the degradation at the high heating rates met in the combustion could be determined and the gap to analytical techniques such as thermogravimetry bridged. The interplay of mechanical char integrity and heat feedback by the flame determined how much time the specimen dwells in temperature range of 300 to 420 C where char expansion due to calcium salt formation is effective and thereby affects the heat release rate strongly. Vertical cone calorimeter and vertical flame testing were used to assess melt dripping and char stability under flaming combustion. Plateeplate rheological measurements proofed to be of limited use to compare the effect of different degradation atmospheres on the melt viscosity. The EMAA formulation had the most effective intumescent process with a low heat release rate and good char stability even in vertical configuration. Electron-beam irradiated EMAA specimens with different levels of

cross-links were tested in the cone calorimeter in order to understand the role of cross-links for the intumescent process.

Publiceringsår

2007

Språk

Engelska

Sidor

1899-1910

Publikation/Tidskrift/Serie

Polymer Degradation and Stability

Volym

92

Issue

10

Dokumenttyp

Artikel i tidskrift

Förlag

Elsevier

Ämne

  • Building Technologies
  • Other Civil Engineering

Nyckelord

  • Chalk
  • Intumescence
  • Polyolefin
  • Acrylic
  • Flame retardant
  • Halogen-free