Simulation of corrosion fatigue crack growth under mixed-mode loading

In English

Författare

Summary, in English

The kinking of a corrosion crack due to mixed-mode fatigue loading is studied using an adaptive finite element procedure. The rate of material dissolution is assumed to be proportional to the stretching of the corroding surface. The dissolution of material is governed by a corrosion law, where no criterion is needed for neither crack growth nor growth direction. The problem is treated as a general moving boundary problem. The kink angles are found to be in very good agreement with results for sharp cracks using criteria reported in the literature.

Publiceringsår

2008

Språk

Engelska

Sidor

440-451

Publikation/Tidskrift/Serie

Engineering Fracture Mechanics

Volym

75

Issue

3-4

Dokumenttyp

Artikel i tidskrift

Förlag

Elsevier

Ämne

  • Mechanical Engineering

Nyckelord

  • Crack growth
  • Corrosion fatigue
  • Stress corrosion
  • Kink angle
  • Crack path

Conference name

International Conference on Crack Paths, 2008

Conference date

2008-09-01 - 2008-09-02

Conference place

Parma, Italy

Status

Published

ISBN/ISSN/Övrigt

  • ISSN: 1873-7315