Diameter-Dependent Photocurrent in InAsSb Nanowire Infrared Photodetectors.

In English

Författare

Summary, in English

Photoconductors using vertical arrays of InAs/InAs1-xSbx nanowires with varying Sb composition x have been fabricated and characterized. The spectrally resolved photocurrents are strongly diameter dependent with peaks, which are red-shifted with diameter, appearing for thicker wires. Results from numerical simulations are in good agreement with the experimental data and reveal that the peaks are due to resonant modes that enhance the coupling of light into the wires. Through proper selection of wire diameter, the absorptance can be increased by more than 1 order of magnitude at a specific wavelength compared to a thin planar film with the same amount of material. A maximum 20% cutoff wavelength of 5.7 μm is obtained at 5 K for a wire diameter of 717 nm at a Sb content of x = 0.62, but simulations predict that detection at longer wavelengths can be achieved by increasing the diameter. Furthermore, photodetection in InAsSb nanowire arrays integrated on Si substrates is also demonstrated.

Publiceringsår

2013

Språk

Engelska

Sidor

1380-1385

Publikation/Tidskrift/Serie

Nano Letters

Volym

13

Issue

4

Dokumenttyp

Artikel i tidskrift

Förlag

The American Chemical Society (ACS)

Ämne

  • Nano Technology

Status

Published

ISBN/ISSN/Övrigt

  • ISSN: 1530-6992