Multiblock copolymers with highly sulfonated blocks containing di- and tetrasulfonated arylene sulfone segments for proton-exchange membrane fuel cell applications

Publiceringsår: 2012
Språk: Engelska
Sidor: 129-140
Publikation/Tidskrift/Serie: Advanced Energy Materials
Volym: 2
Nummer: 1
Dokumenttyp: Artikel i tidskrift
Förlag: Wiley-Blackwell


Multiblock copoly(arylene ether sulfone)s with different block lengths and ionic contents are tailored for highly stable and proton conducting electrolyte membranes. Two series of fully aromatic copolymers are prepared by coupling reactions between non-sulfonated hydrophobic precursor blocks and highly sulfonated hydrophilic precursor blocks containing either fully disulfonated diarylsulfone or fully tetrasulfonated tetraaryldisulfone segments. The sulfonic acid groups are exclusively introduced in ortho positions to the sulfone bridges to impede desulfonation reactions, and give the blocks ion exchange capacities (IECs) of 4.1 and 4.6 meq./g, respectively. Solvent cast block copolymer membranes show well-connected hydrophilic nanophase domains for proton transport and high decomposition temperatures above 310 ˚C under air. Despite higher IEC values, membranes containing tetrasulfonated tetraaryldisulfone segments display a markedly lower water uptake than the corresponding ones with disulfonated diarylsulfone segments when immersed in water at 100 ˚C, presumably because of the much higher chain stiffness and glass transition temperature of the former segments. The former membranes have proton conductivities in level of a perfluorosulfonic acid membrane (NRE212) under fully humidified conditions. A membrane with an IEC of 1.83 meq./g reaches above 6 mS/cm under 30% relative humidity at 80 ˚C, to be compared with 10 mS/cm for NRE212 under the same conditions.


  • Chemical Sciences
  • ionomer
  • block copolymer
  • polyelectrolyte
  • sulfonation
  • polycondensation
  • water transport
  • fuel cell membrane


  • ISSN: 1614-6832

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen