Ga sublattice defects in (Ga,Mn)As: Thermodynamical and kinetic trends

Publiceringsår: 2004
Språk: Engelska
Publikation/Tidskrift/Serie: Physical Review Letters
Volym: 93
Nummer: 5
Dokumenttyp: Artikel i tidskrift
Förlag: American Physical Society


We have used positron annihilation spectroscopy and infrared absorption measurements to study the Ga sublattice defects in epitaxial Ga1-xMnxAs with Mn content varying from 0% to 5%. We show that the Ga vacancy concentration decreases and As antisite concentration increases with increasing Mn content. This is in agreement with thermodynamical considerations for the electronic part of the formation energy of the Ga sublattice point defects. However, the absolute defect concentrations imply that they are determined rather by the growth kinetics than by the thermodynamical equilibrium. The As antisite concentrations in the samples are large enough to be important for compensation and magnetic properites. In addition, the Ga vacancies are likely to be involved in the diffusion and clustering of Mn at low annealing temperatures.


  • Physical Sciences
  • Natural Sciences


  • ISSN: 1079-7114

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen