Growth of doped InAsyP1-y nanowires with InP shells

Publiceringsår: 2011
Språk: Engelska
Sidor: 8-14
Publikation/Tidskrift/Serie: Journal of Crystal Growth
Volym: 331
Nummer: 1
Dokumenttyp: Artikel i tidskrift
Förlag: Elsevier


We have studied the growth of doped InAsyP1-y (InAsP) NWs and InAsP-InP core-shell NWs. Using hydrogen chloride (HCl) we were able to prevent radial growth on the InAsP NWs. Undoped and H2S-doped InAsP NWs had almost pure wurtzite crystal structure, while DEZn-doped NWs showed wurtzite periodically separated by short sections of pure zincblende with rotational twins. Electrical measurements confirmed that the H2S-doped and DEZn-doped NWs were highly n- and p-doped, respectively. The core crystal structure strongly influenced the subsequent radial growth of InP shells, and we observed perfectly smooth shells on H2S-doped cores while the zincblende sections resulted in large bulges on the DEZn-doped cores. The average radial growth rate was more than twice as high on the DEZn-doped cores as on the H2S-doped cores. We found that the radial shell growth decreased at increasing temperature, while the axial growth increased. These results demonstrate the importance of the NW core crystal structure for the growth of core-shell NWs. (C) 2011 Elsevier B.V. All rights reserved.


  • Condensed Matter Physics
  • Nanostructures
  • Crystal structure
  • Low pressure metalorganic vapor
  • phase epitaxy
  • Nanomaterials
  • Semiconducting indium compounds
  • Semiconducting III-V materials


  • ISSN: 0022-0248

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen