Studies of resolidification of non-thermally molten InSb using time-resolved X-ray diffraction

Publiceringsår: 2005
Språk: Engelska
Sidor: 893-900
Publikation/Tidskrift/Serie: Applied Physics A: Materials Science & Processing
Volym: 81
Nummer: 5
Dokumenttyp: Artikel i tidskrift
Förlag: Springer


We have used time-resolved X-ray diffraction to monitor the resolidification process of molten InSb. Melting was induced by an ultra-short laser pulse and the measurement conducted in a high-repetition-rate multishot experiment. The method gives direct information about the nature of the transient regrowth and permanently damaged layers. It does not rely on models based on surface reflectivity or second harmonic generation (SHG). The measured resolidification process has been modeled with a 1-D thermodynamic heat-conduction model. Important parameters like sample temperature, melting depth and amorphous surface layer thickness come directly out of the data, while mosaicity of the sample and free carrier density can be quantified by comparing with models. Melt depths up to 80 nm have been observed and regrowth velocities in the range 2-8 m/s have been measured.


  • Atom and Molecular Physics and Optics


  • ISSN: 1432-0630

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen