High quality InAs and GaSb thin layers grown on Si (111)

Publiceringsår: 2011
Språk: Engelska
Sidor: 12-16
Publikation/Tidskrift/Serie: Journal of Crystal Growth
Volym: 332
Nummer: 1
Dokumenttyp: Artikel
Förlag: Elsevier Science BV

Sammanfattning

We have investigated growth of thin epitaxial layers of InAs on Si (1 1 1) substrates by metalorganic vapor phase epitaxy (MOVPE) and successfully grown GaSb layers on InAs. Furthermore, we have studied the effect of growth temperature and material flow on the nucleation stage and also nucleated GaSb nanowires on the underlying GaSb layer. The InAs layers are grown by a standard two-step growth approach. The main parameter under investigation is the effect of incorporating more nucleation layers into the growth process. The addition of more nucleation layers clearly correlates with the surface morphology and quality of the resulting InAs layer. Morphological and structural characterizations prove that a perfect quality InAs layer is achieved by incorporating 4 nucleation layers. Deposited layers with 250 nm thickness and 0.4 nm atomic step roughness have a mobility of 2400 cm(2)/Vs and a carrier concentration of 2.7 x 10(18) cm(-3). Moreover, we have utilized the InAs film to grow a GaSb layer and observed atomic step roughness for a thin film of similar to 300 nm. Finally we demonstrate the growth of GaSb nanowires on the GaSb layer. (C) 2011 Elsevier B.V. All rights reserved.

Disputation

Nyckelord

  • Physics and Astronomy
  • Nucleation
  • Metalorganic vapor phase epitaxy
  • Indium arsenide
  • Gallium
  • antimonide

Övriga

Published
Yes
  • Nano
  • ISSN: 0022-0248

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen