Compositional variation of AlGaN epitaxial films on 6H-SiC substrates determined by cathodoluminescence.

Författare:
Publiceringsår: 2002
Språk: Engelska
Publikation/Tidskrift/Serie: MRS Internet Journal of Nitride Semiconductor Research
Volym: 7
Nummer: 5
Dokumenttyp: Artikel
Förlag: Materials Research Society

Sammanfattning

High quality epitaxial films of A(l)xGa(1-x)N, grown on SiC substrates, were investigated using spatially resolved cathodoluminescence (CL), scanning electron microscopy, and atomic force microscopy. A variation in the observed peak energy position of the CL was related to alloy fluctuations. CL was used to reveal relative alloy fluctuations of approximately 1% on a sub-micrometer scale, with a precision difficult to surpass with other available techniques. By correlating data from the different techniques, a model was derived. The main feature of it is an alloy fluctuation on the micrometer scale, seeded during the initial growth and extending through the epitaxial film. These alloy fluctuations seems to be related to terrace steps ( approximate to5 nm in height), formed preferentially at scratches on the SiC surface. This investigation indicates that the initial growth of epitaxial films is critical and structures formed at the beginning of the growth tend to persist throughout the growth. Further, a strain gradient from the SiC interface extending towards the surface, was observed.

Disputation

Nyckelord

  • Technology and Engineering

Övriga

Published
Yes
  • ISSN: 1092-5783

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen