Controlling the growth of epitaxial graphene on metalized diamond (111) surface

In English

Författare

Summary, in English

The 2-dimensional transformation of the diamond (111) surface to graphene has been demonstrated using ultrathin Fe films that catalytically reduce the reaction temperature needed for the conversion of sp(3) to sp(2) carbon. An epitaxial system is formed, which involves the re-crystallization of carbon at the Fe/vacuum interface and that enables the controlled growth of monolayer and multilayer graphene films. In order to study the initial stages of single and multilayer graphene growth, real time monitoring of the system was preformed within a photoemission and low energy electron microscope. It was found that the initial graphene growth occurred at temperatures as low as 500 degrees C, whilst increasing the temperature to 560 degrees C was required to produce multi-layer graphene of high structural quality. Angle resolved photoelectron spectroscopy was used to study the electronic properties of the grown material, where a graphene-like energy momentum dispersion was observed. The Dirac point for the first layer is located at 2.5 eV below the Fermi level, indicating an n-type doping of the graphene due to substrate interactions, while that of the second graphene layer lies close to the Fermi level. (C) 2015 AIP Publishing LLC.

Publiceringsår

2015

Språk

Engelska

Publikation/Tidskrift/Serie

Applied Physics Letters

Volym

107

Issue

18

Dokumenttyp

Artikel i tidskrift

Förlag

American Institute of Physics (AIP)

Ämne

  • Condensed Matter Physics

Status

Published

ISBN/ISSN/Övrigt

  • ISSN: 0003-6951