The electrical and structural properties of n-type InAs nanowires grown from metal-organic precursors.

Publiceringsår: 2010
Språk: Engelska
Publikation/Tidskrift/Serie: Nanotechnology
Volym: 21
Nummer: 20
Dokumenttyp: Artikel i tidskrift
Förlag: IOP Publishing


The electrical and structural properties of 111B-oriented InAs nanowires grown using metal-organic precursors have been studied. On the basis of electrical measurements it was found that the trends in carbon incorporation are similar to those observed in the layer growth, where an increased As/In precursor ratio and growth temperature result in a decrease in carbon-related impurities. Our results also show that the effect of non-intentional carbon doping is weaker in InAs nanowires compared to bulk, which may be explained by lower carbon incorporation in the nanowire core. We determine that differences in crystal quality, here quantified as the stacking fault density, are not the primary cause for variations in resistivity of the material studied. The effects of some n-dopant precursors (S, Se, Si, Sn) on InAs nanowire morphology, crystal structure and resistivity were also investigated. All precursors result in n-doped nanowires, but high precursor flows of Si and Sn also lead to enhanced radial overgrowth. Use of the Se precursor increases the stacking fault density in wurtzite nanowires, ultimately at high flows leading to a zinc blende crystal structure with strong overgrowth and very low resistivity.


  • Nano Technology


  • ISSN: 0957-4484

Box 117, 221 00 LUND
Telefon 046-222 00 00 (växel)
Telefax 046-222 47 20
lu [at] lu [dot] se

Fakturaadress: Box 188, 221 00 LUND
Organisationsnummer: 202100-3211
Om webbplatsen